Non-monotonous actuation, that is, different kinds of motion in response to a single stimulus, is observed in some natural materials but difficult to implement in synthetic systems. Herein, polymer hydrogel sheets made from polyacrylamide (PAAm) or poly(dimethylacrylamide) (PDMAA) with a cross-linking gradient along the sheet thickness are reported. These are obtained by thermally initiated free radical polymerization using a specially designed Teflon mold with a glass lid. The resulting PAAm hydrogels undergo non-monotonous actuation (rolling into a tube and re-opening) when exposed to aqueous media as a single external stimulus. Their actuation kinetics is tuned with anions that have specific ion effects in their interaction with the surrounding solvent and the polymer itself: structure-breaking chloride enhances the hydration of the polymer backbone, structure-making sulfate decreases it, and is thus slowing down the actuation kinetics of the PAAm hydrogels. The PDMAA gel rolls up instantaneously in aqueous NaCl and only re-opens after 24 h. PDMAA actuation in aqueous Na2 SO4 is only moderate as the gel did not swell in that solvent. Bilayer hydrogels made from PAAm and PDMAA (without gradient) show monotonic actuation, closing in NaCl solution and re-opening in Na2 SO4 .
Keywords: actuators; hydrogels; non-monotonic actuations; polymers; specific ion effects.
© 2023 The Authors. Macromolecular Rapid Communications published by Wiley-VCH GmbH.