Block copolymers utilizing oligomeric poly(pentylene-co-hexylene carbonate)diol modified with 2,4-diisocyanatotoluene and further with 2-bromo-N-(3-hydroxypropyl)-2-methylpropanamide were synthesized and utilized as Activators ReGenerated by Electron Transfer Atom Transfer Radical Polymerization macroinitiators to obtain a first generation of multifunctional recycling additives with poly(glycidyl methacrylate-co-butyl methacrylate-co-methyl methacrylate) side chains, which could act as chain extenders. Then, chosen additive was reacted with a radical scavenger, 3,5-ditertbutyl-4-hydroxybenzoic acid (DHBA), to obtain a second generation of reactive additives. Those copolymers had different numbers of epoxy groups per polymer chain, and different number of epoxides opened with DHBA, hence showed a range of properties, and were utilized as reactive modifiers for polylactide (PLA) extrusion melting. The first-generation modifiers caused an increase in PLA's blends relative melt viscosity, stabilized material properties, and enhanced impact strength, while the second-generation modifiers with more than 8 % of epoxide ring opened showed worse properties. However, they managed to suppress the UV degradation of PLA blend plates.
Keywords: block copolymers; mechanical properties; polymerization; radical reactions; waste prevention.
© 2023 The Authors. ChemSusChem published by Wiley-VCH GmbH.