The deposition/stripping behavior of lithium metal is intriguing, and the associated formation of inactive lithium at various temperatures remains elusive, which hinders the practical application of lithium metal batteries. Here, utilizing the variable-temperature operando solid-state nuclear magnetic resonance (SS NMR) technique, we reveal the temperature effects on the lithium microstructure evolution in a carbonate-based electrolyte system. In addition, the mass spectrometry titration (MST) method is used to quantify the evolution of inactive lithium components, including dead lithium, solid electrolyte interface (SEI), and lithium hydride (LiH). Combined SS NMR and MST results show that the morphology of lithium metal is reasonably correlated to the amount of inactive Li formed. At low/ambient temperature, the lithium microstructure has a similar evolution pattern, and its poor morphology leads to a large amount of dead lithium, which dominates capacity loss; however, at high temperature large and dense lithium deposits form with less dead Li detected, and the intensified electrolyte consumption in SEI formation is the major cause for capacity loss. Our phase-field simulation results reveal that the compact lithium deposition formed at higher temperature is due to the more uniformly distributed electric field and Li+ concentration. Lastly, two strategies in forming a dense Li deposit are proposed and tested that show performance-enhancing results.
Keywords: electrodeposition; failure mechanism; lithium metal anodes; operando NMR; temperature-dependent behavior.