Poly(lactic acid) (PLA) and Poly(butylene succinate) (PBS) were chosen as raw materials and melt blended by a twin screw extruder and pelletized; then, the pellets were extruded into filaments; after that, various PBS/PLA blending samples were prepared by Fused Deposition Molding (FDM) 3D printing technology using the filaments obtained and the effect of the dosage of PBS on technological properties of 3D-printed specimens was investigated. For comparison, the PLA specimen was also prepared by FDM printing. The tensile strength, tensile modulus, thermal stability, and hydrophilicity became poorer with increasing the dosage of PBS, while the flexural strength, flexural modulus, impact strength, and crystallinity increased first and then decreased. The blend containing 10% PBS (10% PBS/PLA) had the greatest flexural strength of 60.12 MPa, tensile modulus of 2360.04 MPa, impact strength of 89.39 kJ/m2, and crystallinity of 7.4%, which were increased by 54.65%, 61.04%, 14.78%, and 51.02% compared to those of printed PLA, respectively; this blend also absorbed the least water than any other specimen when immersed in water. Different from the transparent PLA filament, 10% PBS/PLA filament presented a milky white appearance. The printed 10% PBS/PLA specimen had a smooth surface, while the surface of the printed PLA was rough. All the results indicated that the printed 10% PBS/PLA specimen had good comprehensive properties, including improved mechanical properties, crystallization performance, and surface quality than PLA, as well as proper wettability and water absorption. The prominent conclusion achieved in this work was that 10% PBS/PLA should be an ideal candidate for biodegradable feedstock among all the PBS/PLA blends for FDM 3D printing.
Keywords: 3D printing; blend; fused deposition molding; poly(butylene succinate); poly(lactic acid); property.