Pectin and alginate satisfy multiple functional requirements in the food industry, especially relating to natural packaging formulation. The continuous need for economic and environmental benefits has promoted sourcing and investigating alternative biomaterials, such as cactus pear mucilage from the cladodes of Opuntia spp., as natural packaging alternatives. The structural and mechanical properties of mucilage, pectin and alginate films developed at a 5% (w/w) concentration were modified by treating the films with calcium (Ca) in the calcium chloride (CaCl2) form. Scanning electron microscopy (SEM) showed the 5% (w/w) 'Algerian' and 'Morado' films to display considerable microstructure variation compared to the 5% (w/w) pectin and alginate films, with calcium treatment of the films influencing homogeneity and film orientation. Treating the alginate films with a 10% (w/w) stock CaCl2 solution significantly increased (p < 0.05) the alginate films' tensile strength (TS) and puncture force (PF) values. Consequently, the alginate films reported significantly higher (p < 0.05) film strength (TS and PF) than the pectin + Ca and mucilage + Ca films. The mucilage film's elasticity was negatively influenced by CaCl2, while the pectin and alginate films' elasticity was positively influenced by calcium treatment. These results suggest that the overall decreased calcium sensitivity and poor mechanical strength displayed by 'the Algerian' and 'Morado' films would not make them viable replacements for the commercial pectin and alginate films unless alternative applications were found.
Keywords: Opuntia ficus-indica; alginate; biopolymer films; cactus pear mucilage; cross-linked; mechanical properties; natural packaging; pectin.