Bio-inspired synaptic behavior simulation in thin-film transistors based on molybdenum disulfide

Yufei Wang; Qi Yuan; Xinru Meng; Yanmei Sun

doi:10.1063/5.0174857

Bio-inspired synaptic behavior simulation in thin-film transistors based on molybdenum disulfide

J Chem Phys. 2023 Nov 14;159(18):184702. doi: 10.1063/5.0174857.

Authors

Yufei Wang^{1

2}, Qi Yuan^{1

2}, Xinru Meng^{1

2}, Yanmei Sun^{1

2}

Affiliations

¹ School of Electronic Engineering, Heilongjiang University, Harbin 150080, China.
² Heilongjiang Provincial Key Laboratory of Micro-nano Sensitive Devices and Systems, Heilongjiang University, Harbin 150080, China.

PMID: 37937938
DOI: 10.1063/5.0174857

Abstract

Synaptic behavior simulation in transistors based on MoS2 has been reported. MoS2 was utilized as the active layer to prepare ambipolar thin-film transistors. The excitatory postsynaptic current phenomenon was simulated, observing a gradual voltage decay following the removal of applied pulses, ultimately resulting in a response current slightly higher than the initial current. Subsequently, ±5 V voltages were separately applied for ten consecutive pulse voltage tests, revealing short-term potentiation and short-term depression behaviors. After 92 consecutive positive pulses, the device current transitioned from an initial value of 0.14 to 28.3 mA. Similarly, following 88 consecutive negative pulses, the device current changed, indicating long-term potentiation and long-term depression behaviors. We also employed a pair of continuous triangular wave pulses to evaluate paired-pulse facilitation behavior, observing that the response current of the second stimulus pulse was ∼1.2× greater than that of the first stimulus pulse. The advantages and prospects of using MoS2 as a material for thin-film transistors were thoroughly displayed.