Aims: To evaluate the impact of conditioning protocols, aluminum trioxide (Al2O3), Er:YAG laser (EYL), and Rosebengal (RB), on the surface roughness (Ra) and shear bond strength (SBS) of polyetheretherketone (PEEK) attached to composite restorations.
Method: Eighty PEEK discs in total were produced and then divided into four groups (n = 20). Group1:Sulfuric acid (SA), Group 2: PDT (RB), Group 3: Al2O3, Group 4 EYL, respectively. The Ra of PEEK discs was evaluated using the surface profilometer. After being luted, the discs were attached to composite resin discs. After that, samples were put to SBS testing on a Universal testing apparatus. A stereo microscope was also used to evaluate the type of breakdown. The data were analyzed using Tukey's test and one-way analysis of variance.
Results: The SA treated group exhibited the highest Ra. Nevertheless, the RB specimens activated by PDT treatment had the lowest mean Ra score. The group that received the treatment of SA exhibited the highest average score of SBS. In contrast, specimens treated with PDT and activated by RB exhibited the lowest levels of bond fidelity. Cohesive failure emerges as the prevailing kind of fracture within the various groups subjected to testing.
Conclusion: The utilization of Al2O3, RB activated by PDT, and EYL shows promise as a viable substitute for Sulfuric acid in enhancing the bond integrity of composite cement and surface roughness in PEEK materials.
Keywords: Al(2)O(3); Er:YAg laser; PEEK; Photodynamic therapy; Rosebengal; Surface roughness.