Preparation of Ge-Sb-Se glass fibers with excellent bending properties by the pulsated orifice ejection method

Abstract

We have innovatively introduced the pulsated orifice ejection method into the preparation of glass fibers, successfully preparing high-purity Ge₂₈Sb₁₂Se₆₀ glass fibers. These fibers have a smooth surface, uniform elemental distribution, and excellent bending properties, with a minimal bending radius of 2 mm. In the infrared spectrum from 2.5 to 13.5 µm, the fibers achieve 65% transmission. Additionally, the fibers possess a density of 4.586 g/cm³, a diameter of 35 µm, a glass transition temperature (Tg) of 369°C, and an onset crystallization temperature (Tx) of 557°C. We have also measured the surface tension of the glass fibers, finding values from 0.288 N/m to 0.124 N/m as temperatures rose from 450°C to 500°C. The POEM holds the potential to achieve fiber cores of lengths up to hundreds of meters in theory. Our work provides a distinctive perspective for the preparation of glass fibers.