To investigate the influence of polypropylene-basalt hybrid fibers (PBHFCC) on the durability of ceramsite concrete, this study determined the appearance change, mass loss rate, relative dynamic elastic modulus, compressive strength and splitting tensile strength of ceramsite concrete with four kinds of hybrid fibers volume admixture under chloride erosion and dry-wet cycles. The results reveal that under this effect, the apparent damage of each group of specimens increased with the growth of the erosion time. The quality, compressive strength and splitting tensile strength of the specimens all increased gradually during the erosion age period of the first 72 d and gradually decreased after 72 d. The relative dynamic elastic modulus was similarly mutated in 48 d. When the hybrid fiber content of the specimens is 0.15 vol %, the enhancement effect of ceramsite concrete is better than that of the other three amounts. The relative dynamic elastic modulus value is used as a damage variable to establish the damage equation, and the damage evolution equation of PBHFCC considering the volume of hybrid fiber under chloride erosion and dry-wet cycle is derived. The conclusions can be used as a reference for the durability design and construction of PBHFCC.
Keywords: PBHFCC; chloride erosion; dry–wet cycle; durability damage evolution equation; durability damage test.