Acrylated natural rubber (ANR) with various acrylate contents (0.0-3.5 mol%) was prepared from natural rubber as a raw material and then incorporated with commercial 3D resin to fabricate specimens using digital light processing. As a result, the utilization of ANR with 1.5 mol% acrylate content could provide the maximum improvement in stretchability and impact strength, approximately 155% and 221%, respectively, over using pure 3D resin, without significant deterioration of tensile modulus and mechanical strength. According to evidence from a scanning electron microscope, this might be due to the partial interaction between the dispersed small rubber particles and the resin matrix. Additionally, the glass-transition temperature of the 3D-printed sample shifted to a lower temperature by introducing a higher acrylate content in the ANR. Therefore, this work might offer a practical way to effectively enhance the properties of the fundamental commercial 3D resin and broaden its applications. It also makes it possible to use natural rubber as a bio-based material in light-based 3D printing.
Keywords: acrylated natural rubber; bio-based material; digital light 3D printing processing; modified natural rubber; natural rubber.