This study aimed to examine depth of cure (DoC), mass change, water sorption and solubility of dual-cured bulk-fill restorative materials (Surfil One and Activa) in comparison with a light-cured bulk-fill composite (Filtek One Bulk-Fill) and a resin-modified glass ionomer (Fuji II LC). Twenty specimens were prepared of each material using stainless steel molds designed with a slot (8 × 4 × 2 mm) and irradiated for either 20 or 40 s. The Vickers hardness (VHN) was measured at every 0.5 mm to assess the DoC after 24 h of storage at 37 °C. The depth of cure was reported as the depth corresponding to 80% of the maximum Vickers hardness. Disc-shaped specimens were prepared of each material (n = 5) to investigate mass change, sorption and solubility after 4 months of water storage. The data were analyzed using a two-way and one-way analysis of variance (ANOVA) followed by the Tukey post hoc test (p ≤ 0.05). Fuji II LC had the greatest DoC while Activa had the lowest. The two different irradiation times did not demonstrate a significant difference in DoC for all dual-cured materials (p > 0.05). Fuji II LC had the highest sorption while Filtek One showed the lowest. Surefil One and Fuji II LC had a negative solubility. This study concluded that dual-cured materials showed different depth of cure values despite having the same setting reaction. Both materials exhibited a high water sorption, which might jeopardize their dimensional stability and effect their clinical performance.
Keywords: depth of cure; dual cured; hardness; solubility; sorption.