Objective: Assessment of post surface conditioners [sulfuric acid (SA), Rose Bengal (RB), and sandblasting (SB)] and different luting cements [methyl methacrylate (MMA)-based cement and composite-based cement] on pushout bond strength (PBS) of poly-ether ether-ketone (PEEK) post bonded to canal dentin. Materials and methods: Endodontic treatment was performed on 120 single-rooted human premolar teeth. The preparation of the post space was performed and 4 mm of gutta-percha was retained in the apical region of the root. One hundred and twenty PEEK posts were fabricated from a PEEK blank utilizing a Computer aided design-Computer aided manufacture (CAD-CAM) system. The PEEK posts were allocated randomly into four groups based on post surface conditioning (n = 30). Group A: SA, Group B: RB, Group C: SB, and Group D: No conditioning (NC). Each group was further divided into two subgroups based on the luting cement used for bonding (n = 15). Group A1, B1, C1, and D1 specimens were cemented using composite-based resin cement. However, Group A2, B2, C2, and D2 posts were luted with MMA-based resin cement. PBS assessment using a universal testing machine was performed. Failure modes were analyzed under a stereomicroscope. The data relating to the effects of surface treatment and luting types of cement were analyzed using one-way analysis of variance (ANOVA) and Tukey's post hoc test (p = 0.05). Results: Coronal section of Group B2: RB+Super-Bond C&B [9.61 ± 0.75 megapascals (MPa)] displayed the highest bond scores of PEEK after root dentin. Whereas it was also discovered that Group D1: NC+Panavia®V5 (2.05 ± 0.72 MPa) presented the lowest PBS scores. Intergroup comparison analysis revealed that Group A2: SA+Super-Bond C&B and Group B2: RB+Super-Bond C&B displayed no significant difference in their bond scores. Conclusions: RB and SA possess the potential to be used as a PEEK post conditioner. MMA-based cement displayed better performance than composite-based cement.
Keywords: Rose Bengal; photodynamic therapy; poly-ether ether-ketone; sandblasting; sulfuric acid.