In In this study, the optical properties of magnesium-aluminate spinel were examined after being irradiated with 220 MeV Xe ions. The research aimed to simulate the impact of nuclear fuel fission fragments on the material. The following measurements were taken during the experiments: transmission spectra in the IR region (190-7000) nm, optical absorption spectra in the range (1.2-6.5) eV, and Raman spectra were measured along the depth of ion penetration from the surface to 30 µm. A peak with a broad shape at approximately 5.3 eV can be observed in the optical absorption spectrum of irradiated spinel crystals. This band is linked to the electronic color centers of F+ and F. Meanwhile, the band with a maximum at ~(3-4) eV is attributed to hole color centers. Apart from the typical Raman modes of an unirradiated crystal, additional modes, A1g* (720 cm-1), and Eg* (385 cm-1), manifested mainly as an asymmetric shoulder of the main Eg mode, are also observed. In addition, the Raman spectroscopy method showed that the greatest disordering of crystallinity occurs in the near-surface layer up to 4 μm thick. At the same time, Raman scattering spectroscopy is sensitive to structural changes almost up to the simulated value of the modified layer, which is an excellent express method for certifying the structural properties of crystals modified by swift heavy ions.
Keywords: Raman spectra; absorption spectra; radiation defects; single crystals MgAl2O4; swift heavy ions.