Designing a solid-state electrolyte that satisfies the operating requirements of solid-state batteries is key to solid-state battery applications. The consensus is that solid-state electrolytes need to allow fast ion transport, while providing better interfacial compatibility and mechanical tolerance. Herein, a simple but effective strategy is proposed, combining hard and soft component polymer systems, to exploit a solid polymer electrolyte (SPE) with a 3D network via an in situ graft polymerization. The 3D structure is constructed by a hard cellulose nanocrystal (CNC) as the skeleton and a soft polyacrylonitrile (PAN) as the filler through a dry-processing method. The reported systems have several advantages, including ease of processing, only requiring using an exceedingly small amount of solvent, light weight (ρ = 1.2 g cm-3), excellent mechanical stability (tensile strength of 9.5 MPa), and high ionic conductivity (3.9 × 10-4 S cm-1, 18 °C) and migration number (tLi+ = 0.8). In particular, the high conductivity is enabled: the efficient Li+ transportation path constructed between CNC-PAN powders and abundant sulfonate radicals and hydroxyl groups on the CNC surface acts as the bridge of Li+ transition. When the CNCs are grafted onto the PAN polymer, the dipole-dipole interaction between the nitrile groups of the PAN and the hydroxyl groups of the CNCs can help to improve the mechanical stability and ionic conductivity of the SPE. Moreover, a tightly formed interface between SPE and LiFePO4 (LFP)/carbon black/SPE cathode can be achieved in an assembled solid-state battery by hot pressing, thus further enhancing the battery's performance.
Keywords: cellulose nanocrystal; dry process; ionic conductivity; lithium metal battery; self-assembly; solid polymer electrolyte.