Wound healing using an alginate-based biopolymeric film is one of the most preferred treatments. However, these films lack mechanical strength (elasticity and tensile strength), show higher initial burst release, and exhibit high vapor permeability. The present study reports the development of nanosheets derived from titanium diboride (10 nm) (NTB)-incorporated biopolymeric films (0.025, 0.05, and 0.1% w/v) using sodium alginate (SA) and carboxymethyl cellulose (CMC) to overcome the shortfalls. The surface properties of the film, nanosheet distribution within the film, and possible interactions with the film are explored by using scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), Fourier transform infrared (FTIR), and X-ray diffraction (XRD). These analyses confirm that nanosheets are uniformly distributed in the film and introduce unevenness on the film's surface. The tensile strength of the nanosheet-incorporated film (0.1% NTB film) using UTM is found to be 24.30 MPa (six times higher compared to the blank film), equivalent to human skin. The water vapor transmission rate of the film is also found to be in the desired range (i.e., 2000-2500 g/m2 day). The biocompatibility of the NTB film is confirmed by the MTT assay test using NIH/3T3 cells and HEK 293 cells. Furthermore, the scratch assay shows that the developed films promote cell migration and proliferation. The antibacterial activity of the film is also demonstrated using a model drug, tetracycline hydrochloride (TCl). Besides, the film exhibits the sustained release of TCl and follows the Korsmeyer-Peppas model for drug release. Overall, the 0.1% w/v NTB film is easy to fabricate, biocompatible and shows superior mechanical properties.
Keywords: biopolymers; films; mechanical properties; nanofillers; nanosheets derived from TiB2; sustained release property; wound healing.