The development of technologies capable of producing efficient and economically viable anodes is essential for the electrochemical treatment of water contaminated with complex organic pollutants. In this context, the use of ionic liquids as solvents to prepare mixed metal oxide (MMO) anodes has proven to be an up-and-coming alternative. Here, we analyze the influence of the temperature of calcination (300, 350, and 400 ºC) on the production of Ti(RuO2)0.8-(Sb2O4)0.2 anodes made using the thermal decomposition method using three ionic liquids (IL) as solvents: dipropyl ammonium acetate (DPA-Ac), dipropyl ammonium propionate (DPA-Pr), and dipropyl ammonium butyrate (DPA-Bu). The decomposition temperature for all IL, accessed by thermogravimetry, is below 200 ºC. Physical and electrochemical analyses demonstrate that the calcination temperature of the anodes is decisive for their durability and electrochemical properties. Anodes prepared with DPA-Bu at 350 ºC show higher stability (around 35 h) than those made with other ILs at temperatures of 300 and 400 ºC and improved results in terms of 4-NP mineralization, where 97% of TOC removal was achieved in 120 min. It could be verified that the calcination temperature and IL employed had a decisive influence on the characteristics of the presented anodes. Therefore, the anode prepared with DPA-Bu at 350 ºC is promising for application in the degradation of organic compounds.
Keywords: 4-Nitrophenol; Electrochemical oxidation; Mixed metal oxide anodes; Thermal decomposition.
© 2023. The Author(s), under exclusive licence to Springer-Verlag GmbH Germany, part of Springer Nature.