The electrocatalytic conversion of biomass into high-value-added chemicals is one of the effective methods of green chemistry. Conventional metal catalysts have disadvantages, such as low atomic utilization and small surface areas. Catalyst materials derived from metal-organic frameworks (MOFs) have received much attention due to their unique physicochemical properties. Here, an MOF-derived non-precious metal CoxNiyS electrocatalyst was applied to the oxidation of biomass-derivative 5-hydroxymethylfurfural (HMF). The HMF oxidation reaction activities were modulated by regulating the content of Co and Ni bimetals, showing a volcano curve with an increasing proportion of Co. When the Co:Ni ratio was 2:1, the HMF conversion rate reached 84.5%, and the yield of the main product, 2,5-furandicarboxylic acid (FDCA), was 54%. The XPS results showed that the presence of high-valent nickel species after electrolysis, which further proved the existence and reactivity of NiOOH, as well as the synergistic effect of Co and Ni promoted the conversion of HMF. Increasing the content of Ni could increase the activity of HMF electrochemical oxidation, and increasing the content of Co could reduce the increase in the anodic current. This study has important significance for designing better HMF electrochemical catalysts in the future.
Keywords: 2,5-furandicarboxylic acid; 5-hydroxymethylfurfural oxidation; MOF-derived electrocatalyst; biomass conversion; electrocatalysis.