The main objective of this article is to provide new information on the effects of mechanical pretreatment of AZ80 magnesium alloy ground with SiC emery papers of different grain sizes on the plasma electrolytic oxidation (PEO) process and corrosion properties of AZ80 in 0.1 M NaCl solution. Then, the roughness of the coated samples was measured by confocal microscopy. The corrosion properties of the ground and coated surfaces were determined by potentiodynamic polarization (PDP) within 1 h of exposure, and electrochemical impedance spectroscopy (EIS) was performed during 168 h of exposure at laboratory temperature. Consequently, the obtained results of the PDP measurements were evaluated by the Tafel analysis and the EIS evaluation was performed by the equivalent circuit analysis through Nyquist diagrams. The morphology and structure of PEO coatings were observed by scanning electron microscopy (SEM) through the secondary imaging technology, and the presence of certain elements in PEO coatings was analyzed by EDS analysis.
Keywords: corrosion; electrochemical impedance spectroscopy; magnesium alloys; plasma electrolytic oxidation.