This study aimed to determine the reinforcing effect of two weight ratios of Gum Arabic (GA) natural biopolymer, i.e., 0.5% and 1.0% in the powdered composition of glass ionomer luting cement. GA powder was oxidized and GA-reinforced GIC in 0.5 and 1.0 wt.% formulations were prepared in rectangular bars using two commercially available GIC luting materials (Medicem and Ketac Cem Radiopaque). The control groups of both materials were prepared as such. The effect of reinforcement was evaluated in terms of microhardness, flexural strength (FS), fracture toughness (FT), and tensile strength (TS). The internal porosity and water contact angle formation on the study samples were also evaluated. Film thickness was measured to gauge the effect of micron-sized GA powder in GA-GIC composite. Paired sample t-tests were conducted to analyze data for statistical significance (p < 0.05). The experimental groups of both materials containing 0.5 wt.% GA-GIC significantly improved FS, FT, and TS compared to their respective control groups. However, the microhardness significantly decreased in experimental groups of both cements compared to their respective control groups. The addition of GA powder did not cause a significant increase in film thickness and the water contact angle of both 0.5 and 1.0 wt.% GA-GIC formulations were less than 90o. Interestingly, the internal porosity of 0.5 wt.% GA-GIC formulations in both materials were observed less compared to their respective control groups. The significantly higher mechanical properties and low porosity in 0.5 wt.% GA-GIC formulations compared to their respective control group indicate that reinforcing GA powder with 0.5 wt.% in GIC might be promising in enhancing the mechanical properties of GIC luting materials.
Keywords: film thickness; glass ionomer cement; gum arabic; luting cement; mechanical properties; physical properties.