Polyethylene degradation and heavy metals leaching under realistic tropical marine climate

Abstract

The study examines the influence of temperature and pH on the leaching of six heavy metals (HMs) species: aluminum (Al), zinc (Zn), chromium (Cr), copper (Cu), lead (Pb) and arsenic (As) from transparent polyethylene pellets into seawater. The idea is to understand the potential influence of intensifying global warming and ocean acidification towards microplastic toxicity in the ocean. HMs leaching was obvious by 24th hours, with most HMs concentration decreased in water by 120th and 240th hours except Al. Nevertheless, we report that temperature and pH do not influence the overall HMs leaching from PE pellets with statistical analysis showing no significance (p < 0.05) between temperature and pH toward HMs concentration. Instead, it is hypothesized that these two parameters may be crucial in promoting heavy metal adsorption onto PE pellets under tropical weathering. However, Field Emission Scanning Electron Microscope (FESEM) revealed that temperature and pH are influential in polymer aging and surficial breakdown where pellets exposed in warm, acidic waters showed the greatest extent of weathering. This study highlights that PE pellets exposed under tropical conditions may accelerate surficial degradation and possibly stimulate HMs adherence to the polymer as a pollution vector. Further consideration of metal behaviour in water and microbial activities is crucial to improve our understanding of microplastic toxicity under tropical weathering.

Keywords: Field emission scanning electron microscope (FESEM); Heavy metals (HMs); Microplastics (MPs); Polyethylene (PE); Tropical.