The construction of novel efficient catalysts for the treatment of organic pollutants in the aqueous environment is essential. The lamellar-like Cu-Al layered double hydroxides (CuAl-LDHs) with various mole ratios were synthesized by a simple route of co-precipitation, and the corresponding degradation characteristic was tested for the removal of tetracycline (TC) using PMS activation. The degradation efficiency of TC over CuAl-LDHs increased up to 93% within 10 min for the Cu/Al mole ratio of 3:1 and almost not changed at a higher mole ratio. For further calcining the optimal catalyst at 300 ℃, the degradation efficiency of TC was found to be increased to 96%. Sulfuric radicals and singlet oxygen were analyzed to be the main reason for the change in degradation characteristics, which was proved by radical quenching experiments and electron paramagnetic resonance technique. The parameters including PMS concentration, catalyst dosage, and reaction temperature on the TC degradation as well as the degradation mechanism for PMS activation were elaborated. The best proportion of CuAl-LDHs owned splendid stability and catalytic activity after reusing, which showed enormous potential in practical application.
Keywords: Calcination Treatment; Catalytic degradation; CuAl-LDHs; Mole ratio; Peroxymonosulfate activation.
© 2023. The Author(s), under exclusive licence to Springer-Verlag GmbH Germany, part of Springer Nature.