We aimed to elucidate the effects of ultraviolet (UV) irradiation on the shear bond strength (SBS) between heat-cured polymethyl methacrylate (PMMA) and a Co-Cr-Mo alloy. Disk-shaped Co-Cr-Mo alloy prepared by casting were subjected to different UV treatment times (0, 15, and 30 min). To determine the effect of UV treatment on surface properties of the alloy, surface roughness, wettability, and chemical compositions were analyzed. To evaluate the SBS, cylindrical PMMA was bonded to the UV-treated alloy, and subsequently subjected to the SBS test after 24 h of storage at room temperature or following 10,000 thermal cycles (n=10/group). After the UV treatment, the surface roughness remained unchanged, but oxidation resulted in the surface exhibiting greater hydrophilic characteristics. The UV-treated group showed significantly higher SBS values than those of the non-treated group (p<0.001). These results suggested that UV treatment-mediated oxidation improved the bond strength between PMMA and Co-Cr-Mo alloy.
Keywords: Co-Cr alloy; PMMA; Shear bond strength; Thermocyling; UV treatment.