Ultraviolet blocking ability, antioxidant and antibacterial properties of newly prepared polyvinyl alcohol-nanocellulose‑silver nanoparticles-ChunJian peel extract composite film

Abstract

In this work, nanocellulose (CNC) from waste water chestnut (WCT) shell was firstly used for preparing nanocomposite films, by using ChunJian peel extract (CJPE) as a green reducing agent to synthesize silver nanoparticles (AgNPs), and then loading them into polyvinyl alcohol-nanocellulose (PVA-CNC) matrix, a multifunctional nanocomposite material that could be used in food packaging was developed. The prepared films were tested for mechanical strength, barrier properties, thermal properties, antibacterial, antioxidant and biocompatibility through various characterizations. The PVA-CNC-AgNPs-CJPE film had good thermostability, mechanical strength, barrier properties, and biocompatibility. Compared with pure PVA film and PVA-CNC film, PVA-CNC-AgNPs-CJPE could shield over 95 % of the UVB (320-275 nm) spectrum and UVC (275-200 nm) spectrum and most of the UVA (400-320 nm). By disk diffusion analysis, the inhibition zones of PVA-CNC-AgNPs-CJPE film against E. coli, P. aeruginosa, S. aureus and E. faecalis were 22.3 mm, 25.0 mm, 22.0 mm and 19.3 mm, respectively. The milk antibacterial simulation test confirmed that PVA-CNC-AgNPs-CJPE film could effectively limit bacterial reproduction and prolong the shelf life of milk. PVA-CNC-AgNPs-CJPE film had excellent UV barrier properties, good antioxidant properties and high-efficiency antibacterial activity, which is expected to be widely used in sustainable nanocomposite food packaging.

Keywords: Antimicrobial ability; Antioxidant; UV-blocking.