Surface-modified graphene oxide-based composites for advanced sequestration of basic blue 41 from aqueous solution

Abstract

Advanced materials for the efficient treatment of textile wastewater need to be developed for the sustainable growth of the textile industry. In this study, graphene oxide (GO) was modified by the incorporation of natural clay (bentonite) and mixed metal oxide (copper-cobalt oxide) to produce GO-based binary and ternary composites. Two binary composites, GO/bentonite and GO/Cu-Co Ox (oxide), and one ternary composite, GO/bentonite/Cu-Co Ox, were characterized by Fourier transform-infrared spectroscopy (FTIR), scanning electron microscope (SEM), energy dispersive spectrometer (EDS) and Brunauer-Emmett-Teller (BET) analysis. The adsorption efficiency of these composites was evaluated against a cationic dye, Basic Blue 41 (BB41). The composites had several surface functional groups, and the ternary composite had tubular porous structures formed by the cross-linking of the bentonite and GO planes. The BET surface area of the ternary composite was 50% higher than that of the GO. The BB41 removals were 92, 89, 80, and 69% for GO/bentonite/Cu-Co oxide, GO/bentonite, GO and GO/Cu-Co oxide, respectively. The pseudo-2nd-order and intraparticle diffusion models best describe the kinetics results, indicating chemisorption and slow pore diffusion-controlled adsorption processes. The Langmuir isotherm-derived adsorption capacity of GO/bentonite/Cu-Co oxide was 351.1 mg/g, which was very close to the measured value. After five consecutive cycles, the ternary composite retained 90% BB41 removal efficiency compared to its 1st cycle. Electrostatic interaction and pore diffusion were predicted to be the controlling mechanisms for the adsorption of the BB41. The GO-based ternary composite can be a feasible and scalable adsorbent for BB41 in wastewater treatment.

Keywords: Adsorption mechanism; Functional groups; Modified graphene oxide; Porous structure; Recyclability.