The purpose of this study was to determine how to control and measure the hierarchical swelling in pulp fibers via electrostatic interactions and localized osmotic pressure. A eutectic solvent system was used to systematically increase phosphate groups in the cell wall. Increase in fiber charge led to an increase in swelling properties, as expected. At a charge value around 180-200 μmol/g the macrofibrils were found to deaggregate. This led to a large jump in mesoscale swelling, from 0.9 to 2.5 mL/g, and surface area, from 400 to 1000 m2/g. This deaggregation was confirmed with X-ray scattering and solute exclusion. A novel thermoporosimetry method was used in the study. This involved splitting the nonfreezing water into two subfractions, thus allowing a more complete analysis of pore structure and surface area. The hydrated surface area for the samples was in the range 1200-1400 m2/g, which agreed well with simulations of aggregated microfibrils. Adding charge to the pulp fibers had a nonlinear effect on handsheet strength properties. This suggests that hierarchical control of fiber swelling may be a useful approach to improve important property pairs such as strength/density in packaging and other commercially important fiber products.
Keywords: Bonding; Bound water; Deaggregation; Macrofibril; Swelling; Thermoporosimetry.
Copyright © 2023. Published by Elsevier Ltd.