The compact sulfur cathodes with high sulfur content and high sulfur loading are crucial to promise high energy density of lithium-sulfur (Li-S) batteries. However, some daunting problems, such as low sulfur utilization efficiency, serious polysulfides shuttling, and poor rate performance, are usually accompanied during practical deployment. The sulfur hosts play key roles. Herein, the carbon-free sulfur host composed of vanadium-doped molybdenum disulfide (VMS) nanosheets is reported. Benefiting from the basal plane activation of molybdenum disulfide and structural advantage of VMS, high stacking density of sulfur cathode is allowed for high areal and volumetric capacities of the electrodes together with the effective suppression of polysulfides shuttling and the expedited redox kinetics of sulfur species during cycling. The resultant electrode with high sulfur content of 89 wt.% and high sulfur loading of 7.2 mg cm-2 achieves high gravimetric capacity of 900.9 mAh g-1 , the areal capacity of 6.48 mAh cm-2 , and volumetric capacity of 940 mAh cm-3 at 0.5 C. The electrochemical performance can rival with the state-of-the-art those in the reported Li-S batteries. This work provides methodology guidance for the development of the cathode materials to achieve high-energy-density and long-life Li-S batteries.
Keywords: lithium-sulfur batteries; molybdenum disulfide; nanosheets; shuttling effect; volmetric capacity.
© 2023 Wiley-VCH GmbH.