Vehicle-integrated photovoltaics (VIPV) are gaining attention to realize a decarbonized society in the future, and the specifications for solar cells used in VIPV are predicated on a low cost, high efficiency, and the ability to be applied to curved surfaces. One way to meet these requirements is to make the silicon substrate thinner. However, thinner substrates result in lower near-infrared light absorption and lower efficiency. To increase light absorption, light trapping structures (LTSs) can be implemented. However, conventional alkali etched pyramid textures are not specialized for near-infrared light and are insufficient to improve near-infrared light absorption. Therefore, in this study, as an alternative to alkaline etching, we employed a nanoimprinting method that can easily fabricate submicron-sized LTSs on solar cells over a large area. In addition, as a master mold fabrication method with submicron-sized patterns, silica colloidal lithography was adopted. As a result, by controlling silica coverage, diameter of silica particles (D), and etching time (tet), the density, height, and size of LTSs could be controlled. At the silica coverage of 40%, D = 800 nm, and tet = 5 min, the reduction of reflectance below 65% at 1100 nm and the theoretical short-circuit current gain of 1.55 mA/cm2 was achieved.
Keywords: Colloidal lithography; Dry etching; Light trapping; Nanoimprint; Solar cell.
© 2023. The Author(s).