This work demonstrated the potential of CNC as a substitute for PEG as an additive in ultrafiltration membrane fabrication. Two sets of modified membranes were fabricated using the phase inversion technique, with polyethersulfone (PES) as the base polymer and 1-N-methyl-2 pyrrolidone (NMP) as the solvent. The first set was fabricated with 0.075 wt% CNC, while the second set was fabricated with 2 wt% PEG. All membranes were characterized using SEM, EDX, FTIR, and contact angle measurements. The SEM images were analyzed for surface characteristics using WSxM 5.0 Develop 9.1 software. The membranes were tested, characterized, and compared for their performance in treating both synthetic and real restaurant wastewater. Both membranes exhibited improved hydrophilicity, morphology, pore structure, and roughness. Both membranes also exhibited similar water flux for real and synthetic polluted water. However, the membrane prepared with CNC gave higher turbidity removal and COD removal when raw restaurant water was treated. The membrane compared well with the UF membrane containing 2 wt% PEG in terms of morphology and performance when synthetic turbid water and raw restaurant water were treated.
Keywords: CNC; COD; PEG; morphology; turbidity; ultrafiltration.