YbBO3is a member of the orthoborate family of materials which contains a triangular arrangement of Yb3+ions. Here we study the physical properties of YbBO3with neutron diffraction, inelastic neutron scattering, specific heat, and ac susceptibility measurements. The neutron diffraction measurements confirm that our samples of YbBO3crystallize in the monoclinic space groupC2/c(#15) which contains two crystallographically distinct Yb3+sites decorating a slightly distorted triangular lattice. Heat capacity and ac susceptibility measurements indicate a potential transition to magnetic order at 0.4 K. In agreement with these observations, neutron diffraction measurements at 0.044 K observe magnetic Bragg peaks which can be indexed by a propagation vector of (0 0 1). Although determining a unique spin configuration corresponding to the observed magnetic Bragg peaks is not possible, model refinements indicate that the ordered moments are likely in the range of 0.4-0.9 μBand, notably, require moments on both Yb sites. In addition to the magnetic Bragg peaks, diffuse scattering at lowQis observed indicating that the transition does not correspond to complete long range magnetic order. The two-site picture for YbBO3is further evidenced by the number of crystal field excitations observed by inelastic neutron scattering measurements. Together these results show that YbBO3is a two-site triangular lattice material with signatures of long-range order as well as shorter ranged spin correlations.
Keywords: magnetic structure; neutron scattering; quantum magnetism; triangular lattice.
Creative Commons Attribution license.