Slot-die coating is regarded as a reliable and potential technology for preparing large-area perovskite solar cells with high efficiency and low cost. Therein, the formation of continuous and uniform wet film is of significance to obtain a high-quality solid perovskite film. In this work, the rheological properties of the perovskite precursor fluid are analyzed. Then, the ANSYS Fluent is introduced to establish an integrated model of internal and external flow fields during the coating process. The model is applicable to all perovskite precursor solutions with near-Newtonian fluids. Based on the theoretical simulation of finite element analysis, the preparation of 0.8 M-FAxCs1-xPbI3, one of the typical large-area perovskite precursor solutions, is explored. Accordingly, this work indicates that the coupling process parameters like the fluid supply velocity (Vin) and coating velocity (V) determine the uniformity that the solution flows out of the slit and is coated onto the substrates, and the coating windows for a uniform and stable perovskite wet film is obtained. For the upper boundary range of the coating windows, the maximum value of V and Vin follows V = 0.003 + 1.46Vin (Vin ≤ 0.1 m/s), while for its lower boundary range, the minimum value of V and Vin is V = 0.002 + 0.67Vin (Vin ≤ 0.1 m/s). When Vin is higher than 0.1 m/s, the film will break due to the excessive V. Finally, the real experiment verifies the accuracy of the numerical simulation. Hopefully, this work is of reference value for the development of the slot-die coating forming process on the perovskite precursor solution approximating Newtonian fluid.
© 2023 The Authors. Published by American Chemical Society.