The influence of thermomechanical stress on the conductivity of indium tin oxide (ITO)-coated polycarbonate (PC) films was investigated. PC is the industry's standard material for window panes. ITO coatings on polyethylene terephthalate (PET) films are the main commercially available option; as such, most investigations refer to this combination. The investigations in this study aim to investigate the critical crack initiation strain at different temperatures and crack initiation temperatures for two different coating thicknesses and for a commercially available PET/ITO film for validation purposes. Additionally, the cyclic load was investigated. The results show the comparatively sensitive behavior of the PC/ITO films, with a crack initiation strain at room temperature of 0.3-0.4% and critical temperatures of 58 °C and 83 °C, with high variation depending on the film's thickness. Under thermomechanical loading, the crack initiation strain decreases with increasing temperatures.
Keywords: ITO; electrochromic device; polycarbonate.