Adapting sustainable construction, which involves responsible consumption of natural resources and reducing carbon emissions, could be a unified action to address the intensifying effects of global warming and the increasing rate of waste pollution worldwide. Aiming to lessen the emission from the construction and waste sector and eliminate plastics in the open environment, a foam fly ash geopolymer with recycled High-Density Polyethylene (HDPE) plastics was developed in this study. The effects of the increasing percentages of HDPE on the thermo-physicomechanical properties of foam geopolymer were investigated. The samples' measured density, compressive strength, and thermal conductivity at 0.25% and 0.50% HDPE content was 1593.96 kg/m3 and 1479.06 kg/m3, 12.67 MPa and 7.89 MPa, and 0.352 W/mK and 0.373 W/mK, respectively. Obtained results are comparable to structural and insulating lightweight concretes with a density of less than 1600 kg/m3, compressive strength of greater than 3.5 MPa, and thermal conductivity of less than 0.75 W/mK. Thus, this research concluded that the developed foam geopolymers from recycled HDPE plastics could be a sustainable alternative material and be optimized in the building and construction industry.
Keywords: compressive strength; density; fly ash; foam geopolymer; microstructure; recycled HDPE; sustainable alternative material; thermal conductivity.