Inconel 718 is a nickel-based superalloy with excellent creep properties and good tensile and fatigue strength. In the field of additive manufacturing, it is a versatile and widely used alloy due to its good processability in the powder bed fusion with laser beam (PBF-LB) process. The microstructure and mechanical properties of the alloy produced by PBF-LB have already been studied in detail. However, there are fewer studies on the creep resistance of additively manufactured Inconel 718, especially when the focus is on the build direction dependence and post-treatment by hot isostatic pressing (HIP). Creep resistance is a crucial mechanical property for high-temperature applications. In this study, the creep behavior of additively manufactured Inconel 718 was investigated in different build orientations and after two different heat treatments. The two heat treatment conditions are, first, solution annealing at 980 °C followed by aging and, second, HIP with rapid cooling followed by aging. The creep tests were performed at 760 °C and at four different stress levels between 130 MPa and 250 MPa. A slight influence of the build direction on the creep properties was detected, but a more significant influence was shown for the different heat treatments. The specimens after HIP heat treatment show much better creep resistance than the specimens subjected to solution annealing at 980 °C with subsequent aging.
Keywords: HIP; Inconel 718; PBF-LB; creep; hot isostatic pressing; post-processing.