Metallic or metal oxide-based nanoparticles have the potential to inactivate viruses. Among various metals, copper has shown edge over others. One of the rapidly evolving areas is to combine nanoscience for production of self-sanitizing antiviral surfaces. In this study, we designed antiviral-coated fabrics to combat the spread of viruses. Copper oxide nanoparticles were sonochemically synthesized and subsequently deposited using the dip-coat process to modify the surface of fabric. The morphology and structure of uncoated and coated fabrics were examined by scanning electron microscopy, X-ray diffraction, FTIR, and elemental analysis. The findings show that small, agglomerated rugby ball structures made of copper oxide (CuO) nanoparticles (16 ± 1.6 nm, according to the Scherrer equation) develop on the surface of fabric, resulting in nano-embossing and a hydrophobic (contact angle > 140°) surface. The CuO-coated fabric yielded the maximum zone of inhibition for antibacterial activity. The virucidal activity (against human adenovirus-B) of CuO nanoparticle-fabricated fabric against adenovirus shows decreased 99.99% according to the ISO 18184 testing standard. With the dip and dry approach, any textile industry can use the simple coating procedure without having to change its textile operations. This fabric can be widely used in the face mask, clothing, bedding, and aprons, and the coating remains efficient over more than 25 washes.
© 2023 The Authors. Published by American Chemical Society.