Li-ion transport and phase transition of solid electrolytes are critical and fundamental issues governing the rate and cycling performances of solid-state batteries. In this work, in-operando high-pressure nuclear magnetic resonance (NMR) spectroscopy for the solid-state battery is developed and applied, in combination with 6 Li-tracer NMR and high-resolution NMR spectroscopy, to investigate the Li10 GeP2 S12 electrolyte under true-to-life operation conditions. The results reveal that the Li10 GeP2 S12 phase may become more disordered and a large amount of conductive metastable β-Li3 PS4 as the glassy matrix in the electrolyte transforms into less conductive phases, mainly γ-Li3 PS4 , when high current densities (e.g., ≥0.5 mA cm-2 ) are applied to the electrolyte. The overall Li-transport also varies and shows a tendency of boundary phases and Li10 GeP2 S12 synergistic dominant conduction at high currents. Accordingly, a mechanism of structural change induced by stress variation due to the drastic morphological change during Li-In alloying at high currents, and the local Li+ diffusion coefficient discrepancy is proposed. These new findings of Li-ion transport and boundary phase transition in Li10 GeP2 S12 solid electrolyte under high-pressure and high current density are first reported and will help provide previously lacking insights into the relationship of structure and performance of Li10 GeP2 S12 .
Keywords: Li-ion transport; Li10GeP2S12; high-pressure nuclear magnetic resonance (NMR); in-operando NMR; phase transition.
© 2023 Wiley-VCH GmbH.