The high reliability and proven ultra-longevity make aqueous hydrogen gas (H2 ) batteries ideal for large-scale energy storage. However, the low alkaline hydrogen evolution and oxidation reaction (HER/HOR) activities of expensive platinum catalysts severely hamper their widespread applications in H2 batteries. Here, cost-effective, highly active electrocatalysts, with a model of ruthenium-nickel alloy nanoparticles in ≈3 nm anchored on carbon black (RuNi/C) as an example, are developed by an ultrafast electrical pulse approach for nickel-hydrogen gas (NiH2 ) batteries. Having a competitive low cost of about one fifth of Pt/C benckmark, this ultrafine RuNi/C catalyst displays an ultrahigh HOR mass activity of 2.34 A mg-1 at 50 mV (vs RHE) and an ultralow HER overpotential of 19.5 mV at a current density of 10 mA cm-2 . As a result, the advanced NiH2 battery can efficiently operate under all-climate conditions (from -25 to +50 °C) with excellent durability. Notably, the NiH2 cell stack achieves an energy density up to 183 Wh kg-1 and an estimated cost of ≈49 $ kWh-1 under an ultrahigh cathode Ni(OH)2 loading of 280 mg cm-2 and a low anode Ru loading of ≈62.5 µg cm-2 . The advanced beyond-industrial-level hydrogen gas batteries provide great opportunities for practical grid-scale energy storage applications.
Keywords: HER/HOR catalysts; all-climate performance; electrical pulse synthesis; grid-scale energy storage; hydrogen gas batteries; long life.
© 2023 Wiley-VCH GmbH.