Calcium alginate (CA) hydrogel spheres were widely used as adsorbents to remove organics, but their adsorption capacities and reusability to some antibiotics are unsatisfactory. In this study, calcium alginate/chitosan (CA/CTS) hydrogel spheres were prepared as precursors. Acid-washed CA/CTS (CA/CTS-M) hydrogel spheres (310.6 mg/g) behaved much better adsorption capacity of norfloxacin (NOR) than CA (69.5 mg/g) and CA/CTS (87.7 mg/g) hydrogel spheres. Astonishingly, after being reused for 15 cycles, CA/CTS-M has no loss of NOR adsorption capacity. In the original idea, acid wash was expected to remove the chitosan in CA/CTS hydrogel spheres for obtaining a larger specific surface area. Both scanning electron microscopy and Brunauer-Emmett-Teller test showed that acid wash can remove CTS from CA/CTS hydrogel spheres to increase the specific surface area. However, part of the chitosan remained in CA/CTS-M, having a role to enhance the structural stability of the material, because the acid-washed CA (about 2 mm) has a significantly smaller diameter than CA/CTS-M (about 3 mm). According to the influence of pH and density functional theory calculations, electrostatic attraction is the key driving force of NOR adsorption. Importantly, acid wash led to more negative-charged surface characterized by Zeta potential, which is the main reason of the significantly enhanced adsorption capacity of CA/CTS-M in removal of NOR. In short, CA/CTS-M hydrogel spheres are environment friendly and highly stable adsorbents with high adsorption capacity in the removal of NOR.
Keywords: Adsorption; Chitosan; Mechanism analysis; Modified calcium alginate; Norfloxacin.
Copyright © 2023 Elsevier Ltd. All rights reserved.