Fully room temperature three-dimensional (3D) shape-reprogrammable, recyclable, and photomobile azobenzene (azo) polymer actuators hold much promise in many photoactuating applications, but their development is challenging. Herein, we report on the efficient synthesis of a series of main-chain azo liquid crystalline polymers (LCPs) with such performances via Michael addition polymerization. They have both ester groups and two kinds of hydrogen bond-forming groups (i.e., amide and secondary amino groups) and different flexible spacer length in the backbones. Such poly(ester-amide-secondary amine)s (PEAsAs) show low glass transition temperatures (Tg ≤ 18.4 °C), highly ordered smectic liquid crystalline phases, and reversible photoresponsivity. Their uniaxially oriented fibers fabricated via the melt spinning method exhibit good mechanical strength and photoinduced reversible bending/unbending and large stress at room temperature, which are largely influenced by the flexible spacer length of the polymers. Importantly, all these fibers can be easily reprogrammed under strain at 25 °C into stable fiber springs capable of showing a totally different photomobile mode (i.e., unwinding/winding), mainly owing to the presence of low Tg and both dynamic hydrogen bonding and stable crystalline domains (induced by the uniaxial drawing during the fiber formation). They can also be recycled from a solution at 25 °C. This work not only presents the first azo LCPs with 3D shape reprogrammability, recyclability, and photomobility at room temperature, but also provides some important knowledge of their structure-property relationship, which is useful for designing more advanced photodeformable azo polymers.
Keywords: azobenzene; main-chain liquid crystalline polymers; photomobile; physically cross-linked; recyclable; reprogrammable; room temperature.