Stiffness variable polymers are an essential family of materials that have aroused considerable attention in soft actuators. Although lots of strategies have been proposed to achieve variable stiffness, it remains a formidable challenge to achieve a polymer with a wide stiffness range and fast stiffness change. Herein, a series of variable stiffness polymers with a fast stiffness change and wide stiffness range were successfully synthesized, and the formulas were optimized via Pearson correlation tests. The rigid/soft stiffness ratio of the designed polymer samples can reach up to 1376-folds. Impressively, owing to the phase-changing side chains, the narrow endothermic peak can be observed with full width at half-maximum within 5 °C. Moreover, the shape memory properties of the shape fixity (Rf) and shape recovery ratio (Rr) values of the shape memory properties could reach up to 99.3 and 99.2%, respectively. Then, the obtained polymer was introduced into a kind of designed 3D printing soft actuator. The soft actuator can achieve sharp heating-cooling cycle of 19 s under a 1.2 A current with 4 °C water as coolant and can lift a 200 g weight at the actuating state. Moreover, the stiffness of the soft actuator can reach up to 718 mN/mm. The soft actuator exhibits an outstanding actuate behavior and stiffness switchable capability. We expect our design strategy and obtained variable stiffness polymers to be potentially applied in soft actuators and other devices.
Keywords: Joule heating; phase changing; shape memory; soft actuator; variable stiffness.