Enhancement of ZnO@RuO2 bifunctional photo-electro catalytic activity toward water splitting

Katarina Aleksić; Ivana Stojković Simatović; Ana Stanković; Ljiljana Veselinović; Stevan Stojadinović; Vladislav Rac; Nadežda Radmilović; Vladimir Rajić; Srečo Davor Škapin; Lidija Mančić; Smilja Marković

doi:10.3389/fchem.2023.1173910

Enhancement of ZnO@RuO₂ bifunctional photo-electro catalytic activity toward water splitting

Front Chem. 2023 Apr 27:11:1173910. doi: 10.3389/fchem.2023.1173910. eCollection 2023.

Affiliations

¹ Institute of Technical Sciences of SASA, Belgrade, Serbia.
² Faculty of Physical Chemistry, University of Belgrade, Belgrade, Serbia.
³ Faculty of Physics, University of Belgrade, Belgrade, Serbia.
⁴ Faculty of Agriculture, University of Belgrade, Zemun, Serbia.
⁵ Vinča Institute of Nuclear Sciences, University of Belgrade, Belgrade, Serbia.
⁶ Jožef Stefan Institute, Ljubljana, Slovenia.

Abstract

Catalytic materials are the greatest challenge for the commercial application of water electrolysis (WEs) and fuel cells (FCs) as clean energy technologies. There is a need to find an alternative to expensive and unavailable platinum group metal (PGM) catalysts. This study aimed to reduce the cost of PGM materials by replacing Ru with RuO₂ and lowering the amount of RuO₂ by adding abundant and multifunctional ZnO. A ZnO@RuO₂ composite in a 10:1 molar ratio was synthesized by microwave processing of a precipitate as a green, low-cost, and fast method, and then annealed at 300°C and 600°C to improve the catalytic properties. The physicochemical properties of the ZnO@RuO₂ composites were investigated by X-ray powder diffraction (XRD), Raman and Fourier transform infrared (FTIR) spectroscopy, field emission scanning electron microscopy (FESEM), UV-Vis diffuse reflectance spectroscopy (DRS), and photoluminescence (PL) spectroscopy. The electrochemical activity of the samples was investigated by linear sweep voltammetry in acidic and alkaline electrolytes. We observed good bifunctional catalytic activity of the ZnO@RuO₂ composites toward HER and OER in both electrolytes. The improved bifunctional catalytic activity of the ZnO@RuO₂ composite by annealing was discussed and attributed to the reduced number of bulk oxygen vacancies and the increased number of established heterojunctions.

Keywords: RuO2; ZnO; composites; photo-electro catalysis; water splitting.