The large sizes of cations and anions of organic salts are the driving force for the application of ionic liquids (organic salts) in harsh salty conditions. Moreover, the formation of crosslinked ionic liquid networks as anti-rust and anticorrosion protective films on the substrate surfaces repels seawater salt and water vapor from their surface to prevent corrosion. In this respect, an imidazolium epoxy resin and polyamine hardener as ionic liquids were prepared by the condensation of either pentaethylenehexamine or ethanolamine with glyoxal and p-hydroxybenzaldehyde or formalin in acetic acid as a catalyst. The hydroxyl and phenol groups of the imidazolium ionic liquid were reacted with epichlorohydrine in the presence of NaOH as a catalyst to prepare polyfunctional epoxy resins. The chemical structure, nitrogen content, amine value, epoxy equivalent weight, thermal characteristics, and stability of the imidazolium epoxy resin and polyamine hardener were evaluated. Moreover, their curing and thermomechanical properties were investigated to confirm the formation of homogeneous, elastic, and thermally stable cured epoxy networks. The corrosion inhibition and salt spray resistance of the uncured and cured imidazolium epoxy resin and polyamine as coatings for steel in seawater were evaluated.
© 2023 The Authors. Published by American Chemical Society.