Anion-exchange membranes (AEMs) are involved in a wide range of applications, including fuel cells and water electrolysis. A straightforward method for the preparation of efficient AEMs consists of polymer functionalization with robust anion-exchange sites. In this work, an aliphatic polyketone was functionalized with 1-(3-aminopropyl)imidazole through the Paal-Knorr reaction, with a carbonyl (CCO %) conversion of 33%. The anion-exchange groups were generated by the imidazole quaternization by using two different types of alkyl halides, i.e., 1,4-iodobutane and 1-iodobutane, with the aim of modulating the degree of crosslinking of the derived membrane. All of the membranes were amorphous (Tg ∼ 30 °C), thermally resistant up to 130 °C, and had a minimum Young's modulus of 372 ± 30 MPa and a maximum of 86 ± 5 % for the elongation at break for the least-crosslinked system. The ionic conductivity of the AEMs was determined at 25 °C by electrochemical impedance spectroscopy (EIS), with a maximum of 9.69 mS/cm, i.e., comparable with that of 9.66 mS/cm measured using a commercially available AEM (Fumasep-PK-130). Future efforts will be directed toward increasing the robustness of these PK-based AEMs to meet all the requirements needed for their application in electrolytic cells.
Keywords: Paal–Knorr; anion-exchange membrane; membranes; polyketone; quaternary ammonium; water electrolysis.