H doping can enhance the performance of ZnO thin-film transistors (TFTs) to a certain extent, and the design of double active layers is an effective way to further improve a device's performance. However, there are few studies on the combination of these two strategies. We fabricated TFTs with ZnO:H (4 nm)/ZnO (20 nm) double active layers by magnetron sputtering at room temperature, and studied the effect of the hydrogen flow ratio on the devices' performance. ZnO:H/ZnO-TFT has the best overall performance when H2/(Ar + H2) = 0.13% with a mobility of 12.10 cm2/Vs, an on/off current ratio of 2.32 × 107, a subthreshold swing of 0.67 V/Dec, and a threshold voltage of 1.68 V, which is significantly better than the performance of single active layer ZnO:H-TFTs. This exhibits that the transport mechanism of carriers in double active layer devices is more complicated. On one hand, increasing the hydrogen flow ratio can more effectively suppress the oxygen-related defect states, thus reducing the carrier scattering and increasing the carrier concentration. On the other hand, the energy band analysis shows that electrons accumulate at the interface of the ZnO layer close to the ZnO:H layer, providing an additional path for carrier transport. Our research exhibits that the combination of a simple hydrogen doping process and double active layer construction can achieve the fabrication of high-performance ZnO-based TFTs, and that the whole room temperature process also provides important reference value for the subsequent development of flexible devices.
Keywords: RF magnetron sputtering; ZnO:H/ZnO double active layers; room temperature; thin-film transistors.