The effect of magnesium (Mg) content on the microstructure, mechanical properties, and cytocompatibility of degradable Zn-0.5Mn-xMg (x = 0.05 wt%, 0.2 wt%, 0.5 wt%) alloys was investigated. The microstructure, corrosion products, mechanical properties, and corrosion properties of the three alloys were then thoroughly characterized by scanning electron microscopy (SEM), electron back-scattered diffraction (EBSD), and other methods. According to the findings, the grain size of matrix was refined by the addition of Mg, while the size and quantity of Mg2Zn11 phase was increased. The Mg content could significantly improve the ultimate tensile strength (UTS) of the alloy. Compared with the Zn-0.5Mn alloy, the UTS of Zn-0.5Mn-xMg alloy was increased significantly. Zn-0.5Mn-0.5Mg exhibited the highest UTS (369.6 MPa). The strength of the alloy was influenced by the average grain size, the solid solubility of Mg, and the quantity of Mg2Zn11 phase. The increase in the quantity and size of Mg2Zn11 phase was the main reason for the transition from ductile fracture to cleavage fracture. Moreover, Zn-0.5Mn-0.2Mg alloy showed the best cytocompatibility to L-929 cells.
Keywords: Mg2Zn11; Zn-Mn-Mg alloys; corrosion properties; cytocompatibility; strength.