In this work, we grafted lysine on PVA electrospun fibers, using a green preparation technique. The resulting fiber mats were proposed for gold nanoparticles (AuNPs) removal from water. The efficiency of three fibers with different lysine amounts (10, 20, and 30%) was investigated. The incorporation of amino groups in PVA fibers was firstly proved by FTIR, SEM, and elemental analysis, confirming the presence of lysine. Among the three different fibers, PVA-LYS 30% has shown the best removal efficiency, reaching 65%, at pH equal to 5. Adsorption isotherms were studied and showed that the Langmuir model is the best model fitting our experimental results, with a maximum adsorption capacity of 20.1 mg g-1. Metal-ligand interactions and electrostatic attraction between protonated amino groups of lysine on the fibers and negatively charged, citrate capped, AuNPs are the main proposed mechanisms for AuNP adsorption on the fibers. Sustainability of AuNPs adsorbed on these fibers has been checked through their reuse as catalyst for the reduction of 4-nitrophenol to 4-aminophenol. The process was completed within 60 min, and their reusability showed more than 99% efficiency after 5 reduction cycles. Our results prove that green PVA-LYS fibers can extract nanoparticles from water, as low cost-effective and eco-friendly adsorbent, and contribute to the promotion of a circular economy approach, through their reuse as catalyst in the reduction of pollutants.
Keywords: Electrospinning; Green cross-linking; Lysine; Nanoparticles; Polyvinyl alcohol; Surface modification.
© 2023. The Author(s), under exclusive licence to Springer-Verlag GmbH Germany, part of Springer Nature.