Designed Production of Atomic-Scale Nanowindows in Single-Walled Carbon Nanotubes

Yuki Nagata; Radovan Kukobat; Ayumi Furuse; Hayato Otsuka; Takuya Hayashi; Katsumi Kaneko

doi:10.1021/acs.langmuir.3c00422

Designed Production of Atomic-Scale Nanowindows in Single-Walled Carbon Nanotubes

Langmuir. 2023 Apr 25;39(16):5911-5916. doi: 10.1021/acs.langmuir.3c00422. Epub 2023 Apr 13.

Authors

Yuki Nagata^{1

2

3}, Radovan Kukobat^{2

4}, Ayumi Furuse², Hayato Otsuka², Takuya Hayashi¹, Katsumi Kaneko²

Affiliations

¹ Department of Science and Technology, Interdisciplinary Graduate School of Science and Technology, Shinshu University, 4-17-1 Wakasato, Nagano 380-8553, Japan.
² Research Initiative for Supra-Materials, Shinshu University, 4-17-1 Wakasato, Nagano 380-8553, Japan.
³ Kotobuki Co., Ltd., Kitakyushu City, Fukuoka 802-8540, Japan.
⁴ Department of Chemical Engineering and Technology, Faculty of Technology, University of Banja Luka, V. S. Stepanovica 73, Banja Luka 78000, Bosnia and Herzegovina.

PMID: 37052535
DOI: 10.1021/acs.langmuir.3c00422

Abstract

The controlled production of nanowindows in graphene layers is desirable for the development of ultrathin membranes. Herein, we propose a single-atom catalytic oxidation method for introducing nanowindows into the graphene layers of single-walled carbon nanotubes (SWCNTs). Using liquid-phase adsorption, copper(II) 2,3,9,10,16,17,23,24-octakis(octyloxy)-29H,31H-phthalocyanine (CuPc) was adsorbed on SWCNT bundles at a surface coverage of 0.9. Subsequently, narrow nanowindows with a number density of 0.13 nm^-2 were produced by oxidation above 550 K, which is higher than the decomposition temperature of bulk CuPc. In particular, oxidation of the CuPc-adsorbed SWCNTs at 623 K increased the surface area from 280 to 1690 m² g^-1 owing to the efficient production of nanowindows. The nanowindow size was estimated to be similar to the molecular size of N₂ based on the pronounced low-pressure adsorption hysteresis in the N₂ adsorption isotherm. In addition, the enthalpy change for the nanowindow-formation equilibrium decreased by 4 kJ mol^-1 when CuPc was present, further evidencing the catalytic effect of the Cu atoms supplied by the adsorbed CuPc molecules.