In this research, the durability performance of sustainable concrete with the incorporation of reactive magnesium oxide (MgO) and fly ash (FA) was evaluated. The partial replacement of cement with these two materials is an appealing solution for the construction sector due to sustainability benefits and shrinkage reduction. The incorporation of FA by partial replacement of cement was carried out at 0%, 15% and 30%. The incorporation of MgO in concrete was carried out at 0%, 5%, 10% and 20%. Two types of MgO were used, one from Australia and another of Spanish origin. These two materials were evaluated in terms of their individual incorporation, and then an evaluation was carried out when the two were simultaneously used. In terms of durability, performance losses between 3% and 95% were obtained in all tests (water absorption by capillarity and immersion, carbonation depth and resistance to chloride penetration). However, over time, the difference in performance relative to the reference concrete tends to decrease due to the slow hydration that characterizes these two alternative materials. It was found that, in most of the tests, no overlapping of the negative effects occurred. In other words, the simultaneous incorporation of MgO and FA caused performance losses lower than the sum of the losses of their individual incorporation.
Keywords: MgO; concrete; durability properties; fly ash.