Rational ligand passivation is essential to achieve a higher performance of weakly confined lead halide perovskite quantum dots (PQDs) via a mechanism of surface chemistry and/or microstrain. In situ passivation with 3-mercaptopropyltrimethoxysilane (MPTMS) produces CsPbBr3 PQDs with an enhanced photoluminescence quantum yield (PLQY, ΦPL) of up to 99%; meanwhile, charge transport of the PQD film can be enhanced by one order of magnitude. Herein, we examine the effect of the molecular structure of MPTMS as the ligand exchange agent in comparison to octanethiol. Both thiol ligands promote crystal growth of PQDs, inhibit nonradiative recombination, and cause blue-shifted PL, while the silane moiety of MPTMS manipulates surface chemistry and outperforms owing to its unique cross-linking chemistry characterized by FTIR vibrations at 908 and 1641 cm-1. Emergence of the diagnostic vibrations is ascribed to hybrid ligand polymerization arising from the silyl tail group that confers the advantages of narrower size dispersion, lower shell thickness, more static surface binding, and higher moisture resistance. In contrast, the superior electrical property of the thiol-passivated PQDs is mostly determined by the covalent S-Pb bonding on the interface.
Keywords: microstrain; perovskite; quantum dot; siloxane; thiol ligand; vinyl.