Carnation-like ZnO was synthesized by the facile precipitation method (at room temperature and in 120 min) to decompose dyes in an aqueous medium. The carnation-like ZnO had a stratified porous structure with a size of about 2-3μm, its petals had a smooth surface with a thickness of 5-10 nm and a width of about 300-500 nm. Ag-ZnO composites were synthesized using glucose with the assistance of PVP. The morphology of Ag-ZnO composites was almost unchanged compared to ZnO. Where, the Ag nanoparticles in the size range of 5-15 nm were uniformly dispersed on the ZnO petals, improving the catalytic ability of the composites in tartrazine (TA) degradation. The influence of Ag content on catalytic structure and performance of composite was studied. The 5Ag-ZnO sample had the highest BET surface area and pore volume and the lowest gap energy (Eg) among the as-synthesized samples. The 5Ag-ZnO sample proclaimed the degradation efficiency in 70 min of 97.8% and thekapof 0.031 min-1. The influences of catalyst content, solution pH, and concentration of dye on the photodegradation efficiency of the composite were thoroughly studied. Besides, the photocatalytic activity of the composite was demonstrated by degrading various organic substances and reusability. In addition, it was compared to a metal-semiconductor catalyst of Au-ZnO and semiconductor-semiconductor catalysts of MoS2-ZnO, Cu2O-ZnO, and SiO2-ZnO. The catalytic mechanism under visible light was proposed.
Keywords: ZnO; carnation; composites; photocatalyst; tartrazine.
© 2023 IOP Publishing Ltd.