Although solid-state batteries (SSBs) are high potential in achieving better safety and higher energy density, current solid-state electrolytes (SSEs) cannot fully satisfy the complicated requirements of SSBs. Herein, a covalent organic framework (COF) with multi-cationic molecular chains (COF-MCMC) was developed as an efficient SSE. The MCMCs chemically anchored on COF channels were generated by nano-confined copolymerization of cationic ionic liquid monomers, which can function as Li+ selective gates. The coulombic interaction between MCMCs and anions leads to easier dissociation of Li+ from coordinated states, and thus Li+ transport is accelerated. While the movement of anions is restrained due to the charge interaction, resulting in a high Li+ conductivity of 4.9×10-4 S cm-1 and Li+ transference number of 0.71 at 30 °C. The SSBs with COF-MCMC demonstrate an excellent specific energy density of 403.4 Wh kg-1 with high cathode loading and limited Li metal source.
Keywords: Covalent Organic Framework; Ion Transport; Nano-Confined Copolymerization; Solid-State Battery; Solid-State Electrolyte.
© 2023 Wiley-VCH GmbH.